The plateau corresponds to an increase in roughness of
approximately 4 nm. As previously reported, these modifications
arise from the oxidation of the polymer sample [27,19]. Notably, it is
worthy to note that the shape of the kinetic curve is similar to those
that reflect the rate of formation of carbonyl photoproducts, as
plotted from the results given in Fig. 4.