Abstract
Composite films of polypropylene (PP) and modified calcium carbonate (CaCO3) were prepared in a twin screw extruder with
particle content varying from 0.5, 1.0, and 1.5 phr. The CaCO3 surface was modified by palmitic acid (PA) at 1, 3, and 5 %wt.
The modified CaCO3 surface was characterized by FTIR and XRD to indicate that the modifier is combined on the CaCO3
surface. The results showed that optimum of PA attached to that CaCO3 surface was 5 %wt. The influence of modified CaCO3
with and without PA of PP film on the mechanical (tensile strength, Young’s modulus and elongation at break), barrier (OP),
thermal (DMTA, DSC), physical (XRD, SEM and OM) properties were studied. The results observed that incorporation of
modified CaCO3 0.5 phr into PP film showed more dispersion than PP with CaCO3. Furthermore, the addition modified CaCO3
increased tensile strength, Young’s modulus, oxygen permeability and melting point from 22.10 MPa, 984.21 MPa, 3.22

ผลลัพธ์ (ไทย) 1:

บทคัดย่อมีเตรียมฟิล์มคอมโพสิตโพรพิลีน (PP) และปรับเปลี่ยนแคลเซียมคาร์บอเนต (CaCO3) ใน extruder แบบสกรูคู่กับเนื้อหาอนุภาคที่แตกต่างจาก 0.5, 1.0 และ 1.5 phr. ผิว CaCO3 ถูกปรับเปลี่ยน โดยกรด palmitic (PA) ที่ 1, 3 และ 5% wtผิว CaCO3 แก้ไขถูกลักษณะ FTIR และ XRD เพื่อบ่งชี้ว่า อยู่รวมกับ CaCO3พื้นผิว ผลลัพธ์ที่แสดงที่เหมาะสมของ PA ที่แนบกับพื้นผิวที่ CaCO3 ได้ 5% wt อิทธิพลของ CaCO3 แก้ไขมี และไม่ มี PA PP ฟิล์มบนเครื่องกล (แรง โมดูลัสของยัง และ elongation ที่แบ่ง), อุปสรรค (OP),ความร้อน (DMTA, DSC), มีศึกษาคุณสมบัติทางกายภาพ (XRD, SEM และออม) ผลการสังเกตที่ประสานปรับเปลี่ยน CaCO3 phr 0.5 เป็นฟิล์ม PP พบแพร่กระจายมากขึ้นกว่า PP กับ CaCO3 นอกจากนี้ การเพิ่มปรับเปลี่ยน CaCO3เพิ่มแรง สาวของโมดูลัส ออกซิเจน permeability และจุดหลอมเหลวจาก 22.10 แรง 984.21 แรง 3.22