Wide-angle X-ray scattering tests (WAXS) were carried out for
all samples after 90 days of ageing (Fig. 6(a)). No diffraction peaks
were observed for neat PLA, PLAe15 wt% and e20 wt% OLA films,
confirming that these materials maintained their amorphous
structure during ageing at the studied conditions.