The mechanical performance of NR/n-TiO2(R) composites was enhanced with an increase of n-TiO2(R) content up to the optimum content at 5 phr (parts per hundred parts of rubber) and then declined
The mechanicalperformance of NR/n-TiO2(R) composites was enhanced with an increase of n-TiO2(R) content up to theoptimum content at 5 phr (parts per hundred parts of rubber) and then declined