Dynamic high pressure microfluidization experiments were
performed on laboratory scale microfluidizer M-100EH-30 (channel
diameter ¼ 75 mm) (Microfluidics Co., Newton, MA). The purified
IDF was dispersed in water to a solid to water ratio 1: 35 and
stirred gently at room temperature overnight, and treated under
the DHPM pressures of 80, 120 and 170 MPa for 3 passes, respectively,
the resultant modified sample (MIDF) was named IDF80,
IDF120 and IDF170 accordingly. 500 mL suspension was used for the
first pass, 400 mL for the second pass because initial 100 mL
Dynamic high pressure microfluidization experiments wereperformed on laboratory scale microfluidizer M-100EH-30 (channeldiameter ¼ 75 mm) (Microfluidics Co., Newton, MA). The purifiedIDF was dispersed in water to a solid to water ratio 1: 35 andstirred gently at room temperature overnight, and treated underthe DHPM pressures of 80, 120 and 170 MPa for 3 passes, respectively,the resultant modified sample (MIDF) was named IDF80,IDF120 and IDF170 accordingly. 500 mL suspension was used for thefirst pass, 400 mL for the second pass because initial 100 mL
การแปล กรุณารอสักครู่..