The bottom image of fig. 11 shows much larger cracks indicating higher thermal residual stresses in case of poorly selected process parameters, especially the pulse shape. It has been observed that a higher inductance in the power circuit causes longer pulse durations for the same discharge energy, leading to the surface cracks.