The stress–strain curves and mechanical properties
of the Z-2 and Z-5–Z-9 compounds are shown in
Figure 7 and Table IV, respectively. E100 and E300 of
the Z-5 compound were improved by 0.671 and
2.390 Nm, respectively, compared to those of the Z-1
compound. On the contrary, for the Z-8 compound,
E100 and E300 decreased by 0.071 and 0.698 Nm,
respectively. This means that 0.3 phr nano-ZnO was
too small to show any effect on the improvement in
the degree of crosslinking compared to 5.0 phr of
ZnO.
The stress–strain curves and mechanical properties
of the Z-2 and Z-5–Z-9 compounds are shown in
Figure 7 and Table IV, respectively. E100 and E300 of
the Z-5 compound were improved by 0.671 and
2.390 Nm, respectively, compared to those of the Z-1
compound. On the contrary, for the Z-8 compound,
E100 and E300 decreased by 0.071 and 0.698 Nm,
respectively. This means that 0.3 phr nano-ZnO was
too small to show any effect on the improvement in
the degree of crosslinking compared to 5.0 phr of
ZnO.