The figures show clearly the presence of sigma phase
at the ferrite austenite interfaces, which are considered as
preferential nucleation sites for the heterogeneous precipitation
of intermetallic compounds. The formation of sigma
phase in duplex stainless steels is described by the decomposition
of δ ferrite through an eutectoid transformation