in view of the
morphological structure, the low strength phenomenon for biocomposites can be associated with the obvious voids due to fibre
debonding and pull-out at the low fibre contents of 5–10 wt%, as
well as prevalent fibre agglomeration at the high fibre contents
of 20–30 wt%.