2. ExperimentalA conventional solid

2. Experimental
A conventional solid state reaction route was applied to
prepare the powders with compositions of Bi0.5(Na0.82K0.18)0.5-
TiO3–xCuO–yNb2O5 (x = 0, 0.01, 0.02, 0.03, 0.04 and 0.05;
y = 0, 0.01, 0.02, 0.03 and 0.04). Powders of Bi2O3, K2CO3,
Nb2O5, TiO2, CuO (99.9%, Kojundo Chemical), and Na2CO3
(99.9%, Cerac Specialty Inorganics) were used raw materials.
The powders were weighed according to the chemical formula,
ball-milled for 24 h in ethanol, and calcined at 800 8C for 2 h.
The calcined powder was pressed into circular disks with a
diameter of 12 mm at 100 MPa. The green compacts were
sintered in covered alumina crucibles at 975 8C for 2 h in air.

ผลลัพธ์ (ไทย) 1:

2. ทดลองใช้เส้นทางปฏิกิริยาสถานะของแข็งทั่วไปเตรียมผงกับองค์ประกอบของ Bi0.5 (Na0.82K0.18) 0.5-TiO3 – xCuO – yNb2O5 (x = 0, 0.01, 0.02, 0.03, 0.04 และ 0.05y = 0, 0.01, 0.02, 0.03 และ 0.04) ผงของ Bi2O3, K2CO3Nb2O5, TiO2, CuO (99.9% เคมี Kojundo), และ Na2CO3(99.9%, Cerac พิเศษ Inorganics) ที่ใช้วัตถุดิบผงชั่งน้ำหนักตามสูตรเคมีลูกปลาย 24 h ในเอทานอล และโค้กที่ 8C 800 สำหรับ 2 hกดโค้กผงลงในดิสก์แบบวงกลมกับการเส้นผ่าศูนย์กลาง 12 มม.ที่ 100 MPa กระชับสีเขียวได้เผาในภาชนะหลังคาอลูมินาที่ 975 8C สำหรับ h 2 ในอากาศ

ผลลัพธ์ (ไทย) 2:

2. การทดลอง
แบบธรรมดาเส้นทางรัฐปฏิกิริยาของแข็งถูกนำมาใช้เพื่อ
เตรียมความพร้อมผงที่มีองค์ประกอบของ Bi0.5 (Na0.82K0.18) 0.5
TiO3-xCuO-yNb2O5 (x = 0, 0.01, 0.02, 0.03, 0.04 และ 0.05;
Y = 0, 0.01, 0.02, 0.03 และ 0.04) ผงของ Bi2O3, K2CO3,
Nb2O5, TiO2, ออกไซด์ (99.9% Kojundo เคมี) และ Na2CO3
(99.9% Cerac Inorganics พิเศษ) ถูกนำมาใช้วัตถุดิบ.
ผงชั่งตามสูตรทางเคมี,
ลูกแป้งเป็นเวลา 24 ชั่วโมง เอทานอลและเผาที่อุณหภูมิ 800 8C เป็นเวลา 2 ชั่วโมง.
ผงเผาถูกกดลงดิสก์วงกลมมี
เส้นผ่าศูนย์กลาง 12 มมที่ 100 MPa อัดสีเขียวที่ถูก
เผาในเบ้าหลอมอลูมิครอบคลุม 975 8C เป็นเวลา 2 ชั่วโมงในอากาศ