Prior to determining film properties, samples were conditioned
at 25◦C and 53% relative humidity (RH) for 48 h. Film moisture
content was determined through the weight loss through which
the film went after a 24 h oven drying at 90◦C. Preliminary experiments showed us that 24 h was enough to dry up samples. The temperature was chosen to avoid loss of plasticizer