Beyond its direct relevance
to stress-corrosion cracking, interest in the dealloying
phenomenon extends to the accelerated
corrosion in aluminum alloy 2024-T3 (Unified
Numbering System, or UNS, A92024) (Ref 9, 10)
and the development of high-surface-area electrodes
(Ref 11) and catalysts (Ref 12, 13).