The mass diffusivity was found to be independent of the relative humidity to which the sample was exposed. Experiments
on silica aerogel coated metal foam samples prepared using different type of metal foams (with different surface areas and pore sizes) showed that the surface area of the substrate does not affect the mass diffusion coefficients.