This may be due to the large thickness of the samples. Hydrolytic
degradation test was performed with samples obtained directly
from the extrusion process with thicknesses varying from 0.25 to
0.8 mm. Therefore, it was more difficult to start hydrolytic degradation because the thickness of the sample in this test is a
critical factor.