Magnesium oxide(MgO)nano-size powder is synthesized using magnesium nitrate hexahydrate and
oxalic acid as precursors with ethanol as a solvent.The process involves gel for mation,drying at 100 1C
for 24 h to form magnesium oxalate dihydrate [a-MgC2O4 2H2O] and its decomposition at 500,600,
800,and 1000 1 C for 2 h to yield MgO powder(average crystallite size 6.5–73.5nm).Thesol–gel
products at various stages of synthesis are characterized for their thermal behaviour , phase,
micro structure, optical absorption , and presence of hydroxyl and other groups like OQCQO, CQO,
C–C, etc.MgO powder is shown to possessanf.c.c.(NaCl-type)structure with lattice parameter
increasing with decrease in crystallite size(tav); typical value being 4.222(2)A˚ for tav 6.5 nm as
against the bulk value of 4.211 A˚ . Infrared absorption has shown MgO to be highly reactive with water.
Also, avariety of F-and M-defect centres found in MgO produce energy levels within the band gap
(7.8eV),whichmakeitattractiveforapplicationinplasmadisplaysforincreasingsecondaryelectron
emission and reducing flickering effects.The possible application of the intermediate sol–gel products,
viz., a-MgC2O4 2H2O and anhydrous magnesium oxalate (MgC2O4) in understanding the plant sand ESR
dosimetry,respectively,has also been suggested
Magnesium oxide(MgO)nano-size powder is synthesized using magnesium nitrate hexahydrate and oxalic acid as precursors with ethanol as a solvent.The process involves gel for mation,drying at 100 1Cfor 24 h to form magnesium oxalate dihydrate [a-MgC2O4 2H2O] and its decomposition at 500,600,800,and 1000 1 C for 2 h to yield MgO powder(average crystallite size 6.5–73.5nm).Thesol–gelproducts at various stages of synthesis are characterized for their thermal behaviour , phase,micro structure, optical absorption , and presence of hydroxyl and other groups like OQCQO, CQO,C–C, etc.MgO powder is shown to possessanf.c.c.(NaCl-type)structure with lattice parameterincreasing with decrease in crystallite size(tav); typical value being 4.222(2)A˚ for tav 6.5 nm asagainst the bulk value of 4.211 A˚ . Infrared absorption has shown MgO to be highly reactive with water.Also, avariety of F-and M-defect centres found in MgO produce energy levels within the band gap(7.8eV),whichmakeitattractiveforapplicationinplasmadisplaysforincreasingsecondaryelectronemission and reducing flickering effects.The possible application of the intermediate sol–gel products,viz., a-MgC2O4 2H2O and anhydrous magnesium oxalate (MgC2O4) in understanding the plant sand ESRdosimetry,respectively,has also been suggested
การแปล กรุณารอสักครู่..
![](//thimg.ilovetranslation.com/pic/loading_3.gif?v=b9814dd30c1d7c59_8619)
Magnesium oxide(MgO)nano-size powder is synthesized using magnesium nitrate hexahydrate and
oxalic acid as precursors with ethanol as a solvent.The process involves gel for mation,drying at 100 1C
for 24 h to form magnesium oxalate dihydrate [a-MgC2O4 2H2O] and its decomposition at 500,600,
800,and 1000 1 C for 2 h to yield MgO powder(average crystallite size 6.5–73.5nm).Thesol–gel
products at various stages of synthesis are characterized for their thermal behaviour , phase,
micro structure, optical absorption , and presence of hydroxyl and other groups like OQCQO, CQO,
C–C, etc.MgO powder is shown to possessanf.c.c.(NaCl-type)structure with lattice parameter
increasing with decrease in crystallite size(tav); typical value being 4.222(2)A˚ for tav 6.5 nm as
against the bulk value of 4.211 A˚ . Infrared absorption has shown MgO to be highly reactive with water.
Also, avariety of F-and M-defect centres found in MgO produce energy levels within the band gap
(7.8eV),whichmakeitattractiveforapplicationinplasmadisplaysforincreasingsecondaryelectron
emission and reducing flickering effects.The possible application of the intermediate sol–gel products,
viz., a-MgC2O4 2H2O and anhydrous magnesium oxalate (MgC2O4) in understanding the plant sand ESR
dosimetry,respectively,has also been suggested
การแปล กรุณารอสักครู่..
![](//thimg.ilovetranslation.com/pic/loading_3.gif?v=b9814dd30c1d7c59_8619)
แมกนีเซียมออกไซด์ ( MgO ) ขนาดของผงนาโนสังเคราะห์โดยใช้ Hexahydrate ไนเตรตแมกนีเซียมเป็นสารตั้งต้นและ
กรดออกซาลิกด้วยเอทานอลเป็นตัวทำละลาย กระบวนการเกี่ยวข้องกับเจล mation , การอบแห้งที่ 100 c
24 h เพื่อฟอร์มแมกนีเซียมออกซาเลต 2 [ a-mgc2o4 2H2O-dx ] และสลายตัวใน 500600
1 , 800 และ 1000 องศาเซลเซียส 2 ชั่วโมงเพื่อผลผลิต MgO ผง ( เฉลี่ยขนาดผลึก 6.5 ) thesol –เจล
73.5nm )ผลิตภัณฑ์ที่ขั้นตอนต่างๆของการสังเคราะห์มีลักษณะพฤติกรรมทางโครงสร้างของเฟส
การดูดซึมแสงขนาดเล็กและการแสดงตนของไฮดรอกซิล และกลุ่มอื่น ๆเช่น oqcqo cqo
, , C และ C etc.mgo ผง แสดงให้ possessanf . C.C . ( ชนิดที่มีโครงสร้างแลตทิซพารามิเตอร์ )
เพิ่มกับลดขนาดผลึก ( หนังสือ ) ; ค่าปกติเป็น 4.222 ( 2 ) ˚สำหรับหนังสือ 6.5 nm เป็น
กับมูลค่าของ 4.211 เป็น˚ . การดูดแสงอินฟราเรดได้แสดงขึ้นเป็นปฏิกิริยาตอบโต้กับน้ำ .
ยัง และศูนย์ m-defect f-and MgO พบในผลิตพลังงานภายในช่องว่างแถบ
( 7.8ev ) , การปล่อยและการลดผลกระทบ whichmakeitattractiveforapplicationinplasmadisplaysforincreasingsecondaryelectron
ริบหรี่ โปรแกรมประยุกต์ที่เป็นไปได้ของกลางโซลเจล
) ,คือ a-mgc2o4 2H2O-dx , และไม่มีน้ำแมกนีเซียมออกซาเลต ( mgc2o4 ) ความเข้าใจในทรายพืช ESR
ค่าตามลำดับ นอกจากนี้ยังได้แนะนำ