A well-known eutectoid reaction takes place in steels. When
binary Fe–C alloys containing about 0.77 wt.% C are cooled
below the eutectoid temperature, the eutectoid reaction takes
place involving the decomposition of austenite into ferrite and
cementite. The product phases of the eutectoid reaction feature
pearlite, comprising lamellar ferrite and cementite [1]. The
pearlite colonies nucleate most easily at the original austenite
grain boundaries. The lattice parameters of M3C carbide are
adopted as a=0.4524 nm, b=0.5089 nm, and c=0.6743 nm.
Orientation relationships (ORs) between the ferrite and cementite
have been well documented in the literature. For example,
Bagaryatsky's OR between the ferrite (α) andM3C (C) is [110]α//
[100]C, [111]α//[010]C and (112)α//(001)C. Isaichev's OR is [111]α//
[010]C and (011)α//(103)C [2–4].

ผลลัพธ์ (ไทย) 3:

ปฏิกิริยาเทกทอยดที่รู้จักกันดีจะเกิดขึ้นในเหล็ก เมื่อเหล็กและโลหะผสมที่ประกอบด้วย C
ไบนารีประมาณ 0.77 % โดยน้ำหนัก C เย็น
ด้านล่างอุณหภูมิเทกทอยด , ปฏิกิริยาเทกทอยดใช้เวลา
สถานที่เกี่ยวข้องกับการสลายตัวของ austenite เป็นเฟอร์ไรท์และ
ซีเมนไตต์ . ผลิตภัณฑ์ขั้นตอนของเทกทอยดปฏิกิริยาคุณลักษณะ
pearlite , ประกอบด้วยการทเฟอร์ไรท์และซีเมนไตต์ [ 1 ]
nucleate pearlite อาณานิคมได้ง่ายที่สุดในต้นฉบับ austenite
เม็ดขอบเขต ตาข่ายพารามิเตอร์ของคาร์ไบด์ เป็น m3c
ประกาศใช้ = 0.4524 nm , B = 0.5089 nm และ c = 0.6743 nm .
ความสัมพันธ์ปฐมนิเทศ ( ORS ) ระหว่างเฟอร์ไรท์และซีเมนไตต์
ได้รับเอกสารดีในวรรณคดี ตัวอย่างเช่น
bagaryatsky หรือระหว่างเฟอร์ไรท์ ( α ) andm3c ( C ) [ 110 ] α / /
[ 100 ] C[ 111 ] α / / [ 010 ] C ( 112 ) α / / ( 001 ) C isaichev หรือ [ 111 ] α / /
[ 010 ] C ( 011 ) α / / ( 103 ) C 2 ) [ 4 ]