Objectives. To evaluate the polishing procedures effect on color stability and surface roughness of composite resins. Methods.
Specimens were distributed into 6 groups: G1: Filtek Supreme XT + PoGo; G2: Filtek Supreme XT + Sof-Lex; G3: Filtek Supreme
XT + no polishing; G4: Amelogen + PoGo; G5: Amelogen + Sof-Lex.; G6: Amelogen + no polishing. Initial color values were
evaluated using the CIELab scale. After polishing, surface roughness was evaluated and the specimens were stored in coffee solution
at 37◦C for 7 days. The final color measurement and roughness were determined. Results. Sof-Lex resulted in lower staining.
Amelogen showed the highest roughness values than Filtek Supreme on baseline and final evaluations regardless of the polishing
technique. Filtek Supreme polished with PoGo showed the lowest roughness values. All groups presented discoloration after storage
in coffee solution, regardless of the polishing technique. Conclusion. Multiple-step polishing technique provided lower degree of
discoloration for both composite resins. The final surface texture is material and technique dependent.

ผลลัพธ์ (ไทย) 1:

วัตถุประสงค์ การประเมินผลกระบวนการขัดสีความมั่นคงและพื้นผิวความหยาบของคอมโพสิตเรซิ่น วิธีไว้เป็นตัวอย่างได้กระจายเป็นกลุ่ม 6: G1: Filtek สุพรีม XT + PoGo G2: ฎีกา Filtek XT + Sof-เล็กซ์ทัวร์ G3: Filtek ฎีกาXT + ไม่ขัด G4: Amelogen + PoGo G5: Amelogen + Sof เล็กซ์ทัวร์ G6: Amelogen + ขัดไม่ มีค่าสีเริ่มต้นถูกประเมินโดยใช้มาตราส่วน CIELab หลังจากขัด ความหยาบผิวถูกประเมิน และไว้เป็นตัวอย่างถูกเก็บไว้ในโซลูชันของกาแฟที่ 37◦C 7 วัน มีกำหนดสีขั้นสุดท้ายวัดและความหยาบ ผลลัพธ์ที่ เล็กซ์ทัวร์ Sof ผลในการย้อมสีล่างเห็นค่าความหยาบสูงสุดกว่าฎีกา Filtek ในพื้นฐานและประเมินขั้นสุดท้ายว่าการขัด Amelogenเทคนิคการ ฎีกา Filtek ขัดกับ PoGo ที่แสดงค่าความหยาบต่ำ ทุกกลุ่มนำเสนอกระหลังจากเก็บในโซลูชันกาแฟ โดยเทคนิคขัด สรุป หลายขั้นตอนเทคนิคขัดให้ระดับล่างกระสำหรับเรซิ่นรวมทั้ง ผิวขั้นสุดท้ายจะขึ้นอยู่กับเทคนิคและวัสดุ

ผลลัพธ์ (ไทย) 2:

วัตถุประสงค์ เพื่อประเมินขั้นตอนการขัดผลกระทบต่อความมั่นคงของสีและพื้นผิวที่ขรุขระของเรซินคอมโพสิต . Objectives. To evaluate the polishing procedures effect on color stability and surface roughness of composite resins. Methods.
วิธีการตัวอย่างถูกกระจายออกเป็น6 G2: Filtek G3: Filtek Specimens were distributed into 6 groups: G1: Filtek Supreme XT + PoGo; G2: Filtek Supreme XT + Sof-Lex; G3: Filtek Supreme
XT + G4: Amelogen + PoGo; G5: Amelogen + Sof-Lex .; G6: Amelogen + XT + no polishing; G4: Amelogen + PoGo; G5: Amelogen + Sof-Lex.; G6: Amelogen + no polishing. Initial color values were
evaluated using the CIELab scale. After polishing, surface roughness was evaluated and the specimens were stored in coffee solution
at 37◦C for 7 days. The final color measurement and roughness were determined. Results. Sof-Lex resulted in lower staining.
Amelogen showed the highest roughness values than Filtek Supreme on baseline and final evaluations regardless of the polishing
technique. Filtek Supreme polished with PoGo showed the lowest roughness values. All groups presented discoloration after storage
in coffee solution, regardless of the polishing technique. Conclusion. Multiple-step polishing technique provided lower degree of
discoloration for both composite resins. The final surface texture is material and technique dependent.

ผลลัพธ์ (ไทย) 3:

วัตถุประสงค์ เพื่อประเมินกระบวนการขัดผลต่อความมั่นคง และความขรุขระของผิวสีเม็ดพลาสติกคอมโพสิต วิธี ทำการกระจายออกเป็น 6 กลุ่ม
: G1 : filtek สูงสุด XT Pogo ; G2 : filtek สูงสุด XT Sof เล็กซ์ ; G3 : filtek สูงสุด
XT ไม่ขัดเงา ; G4 : amelogen Pogo ; G5 : amelogen Sof เล็กซ์ ; G6 : amelogen ไม่ขัด ค่าสีเริ่มต้น
ประเมินการใช้แถบมาตราส่วน หลังจากขัดพื้นผิวขรุขระถูกประเมินและทำการเก็บไว้ในสารละลายกาแฟ
37 ◦ C เป็นเวลา 7 วัน สุดท้ายการวัดความหยาบและสีตัวอย่าง ผลลัพธ์ ตัวอย่าง Lex ส่งผลลด staining
amelogen แสดงความหยาบสูงคุณค่ากว่า filtek สูงสุดบนพื้นฐานและการประเมินผลสุดท้ายไม่ว่าขัด
เทคนิคfiltek ฎีกาขัดกับโปโกะ พบค่าความหยาบของค่า ทุกกลุ่มนำเสนอกระหลังกระเป๋า
ในกาแฟสด ไม่ขัด ) สรุป หลายขั้นตอนใช้ขัดให้ลดระดับ
กระทั้งคอมโพสิตเรซิน . พื้นผิวพื้นผิววัสดุ และเทคนิคสุดท้ายคือ
ขึ้นอยู่กับ