Moreover, flux recovery of the fouled PVDF–PVP membranes after cleaned using 3 wt.% NaOH aqueous solution exceeded 90% and was much superior to that of the fouled PVDF membranes.
Moreover, flux recovery of the fouled PVDF–PVP membranes after cleaned using 3 wt.% NaOH aqueoussolution exceeded 90% and was much superior to that of the fouled PVDF membranes.