In contrast to BaTiO3 bulk ceramics, which exhibit a paraelectric to ferroelectric phase transition with decreasing temperature accompanied by a sharp peak of the permittivity at around 123o C, only a broad maximum in the permittivity vs. temperature curve is observed for polycrystalline thin films.