The length of the wear tracks shown in Fig. 8c, is at least 50 mm. Both the V and Cr carbides are considered too small to stop a sliding abrasive particle as their size is limited to 2–4 mm. Fig. 8d shows a cross section of a worn sample from the CT test. Here small grooves are observed indicating that increasing contact pressure leads to microcutting of the PM steel.