The effect of chitosan molecular weight and plasticizer content on moisture sorption behaviour of chitosan thin films was studied. Moisture sorption isotherms were determined at 25 cin the range of 01-09 water activity using a gravimetric method, and the experimental data was used to predict the behaviour of the film under humid conditions. This behaviour was related to the film structure analysed