13. Tension Test Specimens
13.1 For test Bar A, the tension-test specimen A, as shown in Fig. 1, shall be machined concentric with the axis of the test
bar.
13.2 For test Bar B, the tension test specimen B, as shown in Fig. 1, shall be machined concentric with the axis of the test bar.
13.3 For test Bar C, tension test specimens B or C, as shown in Fig. 1, shall be machined concentric with the axis of the test bar. Unless the size of the tension test specimen to be machined from test bar C is specified in writing by the purchaser, the decision whether to use tension test specimen B or C shall be made by the manufacturer of the castings.
13.4 For test bar S, the nature and dimensions of the tension test specimen shall be determined by agreement between the manufacturer and purchaser.
13. Tension Test Specimens13.1 For test Bar A, the tension-test specimen A, as shown in Fig. 1, shall be machined concentric with the axis of the testbar.13.2 For test Bar B, the tension test specimen B, as shown in Fig. 1, shall be machined concentric with the axis of the test bar.13.3 For test Bar C, tension test specimens B or C, as shown in Fig. 1, shall be machined concentric with the axis of the test bar. Unless the size of the tension test specimen to be machined from test bar C is specified in writing by the purchaser, the decision whether to use tension test specimen B or C shall be made by the manufacturer of the castings.13.4 For test bar S, the nature and dimensions of the tension test specimen shall be determined by agreement between the manufacturer and purchaser.