The disappearance of the anhydride

The disappearance of the anhydride peaks of PP-g-MA and the appearance of ester linkage in the FTIR spectra of
the blends indicated interaction between PP, PLA, and PP-g-MA [11]. Confirmation of the blend components
interaction in this study was observed by representing of the ester linkage at 1756-1755 cm-1 (Fig. 2(c-e)). The level
of attractive interaction can also be seen in an increase in the intensity of characteristic absorbance (A) bands [12],
which A is defined as the negative logarithm of the transmittance (T) or A is inverse relation with T [13]. Intensity
reduction of ester linkage transmittance band with increasing of PLA ratio in the blends corresponded to lower
content of ester linkage formation [14]. The absence of this peak could explain the occurrence of thermal chain
scission at C

ผลลัพธ์ (ไทย) 1:

การสูญหายของแห่ง anhydride PP-g-MA และลักษณะที่ปรากฏของการเชื่อมโยงเอสในแรมสเป็คตรา FTIR ของผสมการแสดงโต้ตอบระหว่าง PP ปลา และ PP-g-MA [11] ยืนยันส่วนผสมในการศึกษานี้ถูกตรวจสอบ โดยตัวแทนของการเชื่อมโยงเอสที่ 1756-1755 ซม-1 (Fig. 2(c-e)) ระดับของการโต้ตอบที่น่าสนใจสามารถยังสามารถเห็นได้ในการเพิ่มความเข้มของแถบลักษณะ absorbance (A) [12],ที่ A ถูกกำหนดให้เป็นลอการิทึมลบของ transmittance (T) หรือเป็นความสัมพันธ์ที่ผกผันด้วย [13] ความเข้มลดวง transmittance เชื่อมโยงเอสกับการเพิ่มขึ้นของอัตราส่วนการผสมปลา corresponded ลงเนื้อหาของผู้แต่งเชื่อมโยงเอส [14] การขาดงานสูงนี้สามารถอธิบายการเกิดขึ้นของความร้อนscission ที่ตราสารหนี้ C