2. Experiment2.1. MaterialsCBT resi

2. Experiment
2.1. Materials
CBT resin (CBT 100) is bought from Cyclics Corporation together with 0.6wt.% Tin-based catalyst (PC-4101).
The nano-TiO2 and nano-graphite particles, with an average diameter D of 50nm and 100nm respectively, are
provided by Degussa AG. All materials are dried at 100oC in the vacuum drying oven for 10h to remove the residual
moisture, which could interfere with the polymerization reaction of CBT oligomer. Samples with 0.5wt.% and
1wt.% nano-graphite and 1wt.% and 2wt.% nano-TiO2 are prepared.
2.2. Test method
The crystallization and melting behavior of pCBT are examined with differential scanning calorimeter (DSC) and
thermogravimetric analysis (TGA). The mass of samples is cut from bulk sample in the range of 7-15mg. Nitrogen
is used as the purge gas in the hot stage during all measurements and thermal treatments. Each sample is heated to
260

ผลลัพธ์ (ไทย) 1:

2. ทดลอง2.1. วัสดุยางชุมชน (ชุมชน 100) เป็นซื้อจาก บริษัท Cyclics กับ 0.6wt.% ใช้กระป๋องเศษ (PC-4101)การนาโน TiO2 และแกรไฟต์นาโนอนุภาค กับการเฉลี่ยเส้นผ่าศูนย์กลาง D 50nm และ 100nm จะตามลำดับโดยกโพ AG ทั้งหมดวัสดุจะแห้งที่ 100oC ในการอบแห้งสำหรับ h 10 เพื่อเอาส่วนที่เหลือจากการความชื้น ซึ่งสามารถรบกวนปฏิกิริยา polymerization ของชุมชนยับยั้ง ตัวอย่างที่ มี 0.5wt.% และ1wt.% นาโนแกรไฟต์ และ 1wt.% และ 2wt.% nano-TiO2 เตรียมไว้2.2 การทดสอบวิธีการตกผลึกและละลายพฤติกรรมของ pCBT ตรวจสอบกับแคลอรีมิเตอร์แกนส่วนที่แตกต่าง (DSC) และวิเคราะห์ thermogravimetric (TGA) มวลของตัวอย่างที่ถูกตัดจากตัวอย่างจำนวนมากในช่วงของ 7-15 mg. ไนโตรเจนใช้เป็นแก๊สล้างข้อมูลในระยะร้อนในระหว่างการประเมินและรักษาความร้อนทั้งหมด ตัวอย่างแต่ละอุณหภูมิ260