Fiber pull-out is one of the failure mechanisms in fiber-reinforced composite materials.[1] Other forms of failure include delamination, intralaminar matrix cracking, longitudinal matrix splitting, fiber/matrix debonding, and fiber fracture.[1] The cause of fiber pull-out and delamination is weak bonding