The results observed that incorporation of modified CaCO3 0.5 phr into PP film showed more dispersion than PP with CaCO3. Furthermore, the addition modified CaCO3
increased tensile strength, Young’s modulus, oxygen permeability and melting point from 22.10 MPa, 984.21 MPa, 3.22