Moreover, it is noted
that with the increase of Mg content, the (002) peaks have slightly
shifted to higher diffraction angle, as shown in Fig. 4(b), indicating
an decrease of the lattice constant which is due to the fact that the
ionic radius of Mg2+ (0.57 Å) is smaller than that of Zn2+ (0.60 Å)
[14].