13.11 What is the distinction betwe

13.11 What is the distinction between plastic sheet and film?
Answer. The distinction is based on thickness. Sheet stock has a thickness greater than 0.020 in (0.5
mm), while film stock is less than 0.020 in (0.5 mm) thick.
13.12 What is the blown-film process for producing film stock?
Answer. The blown-film process is a widely used process for making thin polyethylene film for
packaging. It combines extrusion and blowing to produce a tube of thin film. The process begins
with the extrusion of a tube that is immediately drawn upward while still molten and simultaneously
expanded in size by air inflated into it through the die mandrel.
13.13 Describe the calendering process.
Answer. Calendering is a process for producing sheet and film stock out of rubber or rubbery
thermoplastics such as plasticized PVC. In the process, the initial feedstock is passed through a
series of rolls to work the material and reduce its thickness to the desired gage.
13.14 Polymer fibers and filaments are used in several applications; what is the most important application
commercially?
Answer. Textiles.
13.15 Technically, what is the difference between a fiber and a filament?
Answer. A fiber is a long, thin strand of material whose length is at least 100 times its diameter; a
filament is a fiber of continuous length.
13.16 Among the synthetic fiber materials, which are the most important?
Answer. Polyester is the most important commercially, followed by nylon, acrylics, and rayon.
13.17 Briefly describe the injection molding process.
Answer. Injection molding is a process in which a polymer is heated to a highly plastic state and
forced to flow under high pressure into a mold cavity, where it solidifies. The molding is then
removed from the cavity.
13.18 An injection-molding machine is divided into two principal components. Name them.
Answer. The components of an injection-molding machine are (1) the injection unit and (2) the
clamping unit.
13.19 What are the two basic types of clamping units?
Answer. The clamping units are: (1) mechanical toggle clamp and (2) hydraulic. In addition, there
are hydromechanical units which combine hydraulic and mechanical actuations.
13.20 What is the function of gates in injection molds?
Answer. The function of gates in an injection mold is to constrict the flow of molten plastic into the
cavity, which increases the shear rate and reduces the viscosity of the polymer melt.
13.21 What are the advantages of a three-plate mold over a two-plate mold in injection molding?
Answer. As the mold opens, the three-plate mold automatically separates the molded part(s) from
the runner system.
13.22 Discuss some of the defects that can occur in plastic injection molding.
Answer. The defects include (1) short shots, in which the polymer melt solidifies before filling the
cavity; (2) flashing, in which the polymer melt is squeezed into the parting surfaces between the
mold halves and around ejection pins; (3) sink marks, in which the surface is drawn into the molding

ผลลัพธ์ (ไทย) 1:

13.11 อะไรคือความแตกต่างระหว่างพลาสติกแผ่นและฟิล์มคำตอบ แตกขึ้นอยู่กับความหนา หุ้นแผ่นมีความหนามากกว่าใน 0.020 (0.5มม.), ในขณะที่หุ้นฟิล์ม น้อยกว่า 0.020 ใน (0.5 mm) หนา13.12 การเป่าฟิล์มการผลิตฟิล์มหุ้นคืออะไรคำตอบ กระบวนการเป่าฟิล์มเป็นกระบวนการที่ใช้กันอย่างแพร่หลายสำหรับการทำให้ฟิล์มบางบรรจุภัณฑ์ รวมการไหลออกมาและพัดผลิตหลอดของฟิล์มบาง กระบวนการเริ่มต้นมีผงของหลอดที่เป็นทันทีดึงขึ้นในขณะที่ยังหลอมละลาย และพร้อมกันขยายขนาด โดยอากาศที่สูงเกินจริงมาผ่าน mandrel ตาย13.13 อธิบายกระบวนการ calenderingคำตอบ คคอร์ดการเป็นกระบวนการในการผลิตแผ่นและฟิล์มหุ้น จากยาง หรือ rubberythermoplastics เช่น plasticized PVC ในกระบวนการ วัตถุดิบเริ่มต้นได้ผ่านการชุดม้วนวัสดุการทำงาน และลดความหนาของเกจต้อง13.14 เส้นใยพอลิเมอร์และ filaments จะใช้ในแอพพลิเคชันหลาย แอพลิเคชันที่สำคัญที่สุดคืออะไรในเชิงพาณิชย์หรือไม่คำตอบ สิ่งทอ13.15 เทคนิค อะไรคือความแตกต่างระหว่างไฟเบอร์และใยคำตอบ เป็นไฟเบอร์อยู่สแตรนด์ยาว บางของวัสดุที่มีความยาวไม่น้อย 100 เท่าของเส้นผ่าศูนย์กลาง มีใยเป็นใยของความยาวต่อเนื่อง13.16 ระหว่างวัสดุใยสังเคราะห์ ซึ่งเป็นที่สำคัญที่สุดคำตอบ โพลีเอสเตอร์ได้สำคัญสุดในเชิงพาณิชย์ ตาม ด้วยไนล่อน acrylics เรยอง13.17 Briefly describe the injection molding process.Answer. Injection molding is a process in which a polymer is heated to a highly plastic state andforced to flow under high pressure into a mold cavity, where it solidifies. The molding is thenremoved from the cavity.13.18 An injection-molding machine is divided into two principal components. Name them.Answer. The components of an injection-molding machine are (1) the injection unit and (2) theclamping unit.13.19 What are the two basic types of clamping units?Answer. The clamping units are: (1) mechanical toggle clamp and (2) hydraulic. In addition, thereare hydromechanical units which combine hydraulic and mechanical actuations.13.20 What is the function of gates in injection molds?Answer. The function of gates in an injection mold is to constrict the flow of molten plastic into thecavity, which increases the shear rate and reduces the viscosity of the polymer melt.13.21 What are the advantages of a three-plate mold over a two-plate mold in injection molding?Answer. As the mold opens, the three-plate mold automatically separates the molded part(s) fromthe runner system.13.22 Discuss some of the defects that can occur in plastic injection molding.Answer. The defects include (1) short shots, in which the polymer melt solidifies before filling thecavity; (2) flashing, in which the polymer melt is squeezed into the parting surfaces between themold halves and around ejection pins; (3) sink marks, in which the surface is drawn into the molding

ผลลัพธ์ (ไทย) 2:

13.11 อะไรคือสิ่งที่แตกต่างระหว่างแผ่นพลาสติกและฟิล์ม?
คำตอบ ความแตกต่างจะขึ้นอยู่กับความหนา หุ้นแผ่นมีความหนามากกว่า 0.020 ใน (0.5
มิลลิเมตร) ในขณะที่ภาพยนตร์เรื่องหุ้นน้อยกว่า 0.020 ใน (0.5 มิลลิเมตร) หนา.
13.12 อะไรคือสิ่งที่กระบวนการเป่าฟิล์มสำหรับการผลิตฟิล์มหุ้น?
คำตอบ กระบวนการเป่าฟิล์มเป็นกระบวนการที่ใช้กันอย่างแพร่หลายสำหรับการทำฟิล์มพลาสติกบาง ๆ
สำหรับบรรจุภัณฑ์ มันรวมการอัดขึ้นรูปและเป่าในการผลิตหลอดฟิล์มบาง กระบวนการเริ่มต้นด้วยการอัดขึ้นรูปของหลอดที่ถูกวาดขึ้นทันทีในขณะที่ยังหลอมเหลวและพร้อมขยายขนาดทางอากาศที่สูงเกินจริงเป็นมันผ่านเขี้ยวหมูตาย. 13.13 อธิบายขั้นตอน calendering ได้. คำตอบ calendering เป็นกระบวนการในการผลิตแผ่นฟิล์มและหุ้นออกจากยางหรือยางพลาสติกเช่นพลาสติกพีวีซี ในการที่วัตถุดิบเริ่มต้นจะถูกส่งผ่านชุดของการม้วนการทำงานวัสดุและลดความหนาให้กับวัดที่ต้องการ. 13.14 เส้นใยพอลิเมอและเส้นใยที่ใช้ในงานหลายแห่ง สิ่งที่เป็นโปรแกรมที่สำคัญที่สุดในเชิงพาณิชย์? คำตอบ สิ่งทอ. 13.15 เทคนิคอะไรคือความแตกต่างระหว่างเส้นใยและเส้นใยหรือไม่คำตอบ เส้นใยเป็นเวลานานเส้นใยบาง ๆ ของวัสดุที่มีความยาวอย่างน้อย 100 เท่าของเส้นผ่าศูนย์กลางของตน เส้นใยเป็นเส้นใยที่มีความยาวอย่างต่อเนื่อง. 13.16 ท่ามกลางวัสดุเส้นใยสังเคราะห์ซึ่งเป็นสิ่งที่สำคัญมากที่สุด? คำตอบ โพลีเอสเตอร์เป็นเชิงพาณิชย์ที่สำคัญที่สุดตามด้วยไนลอนอะคลิคและเรยอน. 13.17 จงอธิบายขั้นตอนการฉีดขึ้นรูป. คำตอบ การฉีดขึ้นรูปเป็นกระบวนการที่พอลิเมอจะมีความร้อนไปยังรัฐพลาสติกสูงและถูกบังคับให้ไหลภายใต้แรงดันสูงเข้าไปในโพรงแม่พิมพ์ที่มันแข็งตัว ปั้นแล้วลบออกจากโพรง. 13.18 เครื่องฉีดแบ่งออกเป็นสองส่วนหลัก ชื่อพวกเขา. คำตอบ ส่วนประกอบของเครื่องฉีดเป็น (1) หน่วยการฉีดและ (2) หน่วยหนีบ. 13.19 สิ่งที่เป็นสองประเภทพื้นฐานของหน่วยหนีบ? คำตอบ หน่วยหนีบคือ (1) ยึดกลสลับและ (2) ไฮโดรลิค นอกจากนี้ยังมีหน่วย hydromechanical ซึ่งรวม actuations ไฮโดรลิคและเครื่องกล. 13.20 สิ่งที่เป็นหน้าที่ของประตูในแม่พิมพ์ฉีดหรือไม่คำตอบ การทำงานของประตูในแม่พิมพ์ฉีดคือการบีบรัดการไหลของพลาสติกเหลวลงในช่องซึ่งจะเป็นการเพิ่มอัตราการเฉือนและลดความหนืดของการละลายพอลิเมอ. 13.21 อะไรคือข้อดีของแม่พิมพ์สามแผ่นมากกว่าสองแผ่นที่ เชื้อราในการฉีดขึ้นรูป? คำตอบ ในฐานะที่เป็นแม่พิมพ์เปิดแม่พิมพ์สามแผ่นโดยอัตโนมัติแยกส่วนแม่พิมพ์ (s) จากระบบวิ่ง. 13.22 พูดคุยบางส่วนของข้อบกพร่องที่อาจเกิดขึ้นในการฉีดขึ้นรูปพลาสติก. คำตอบ ข้อบกพร่องรวมถึง (1) ภาพระยะสั้นซึ่งละลายพอลิเมอแข็งตัวก่อนที่จะเติมช่อง; (2) กระพริบซึ่งละลายพอลิเมอถูกบีบลงไปในพื้นผิวที่พรากจากกันระหว่างส่วนแม่พิมพ์และรอบขาออก; (3) จมเครื่องหมายที่พื้นผิวจะถูกดึงเข้าไปในการปั้น

ผลลัพธ์ (ไทย) 3:

13.11 อะไรคือความแตกต่างระหว่างแผ่นพลาสติกและฟิล์ม ?
ตอบ ความแตกต่างขึ้นอยู่กับความหนา หุ้นแผ่นมีความหนามากกว่า 0.020 ( 0.5
มม. ) ในขณะที่หุ้นฟิล์มน้อยกว่า 0.020 ( 0.5 มิลลิเมตร ) หนา .
13.12 อะไรคือกระบวนการเป่าฟิล์มผลิตหุ้นฟิล์ม ?
ตอบ โดยกระบวนการเป่าฟิล์ม ใช้กันอย่างแพร่หลาย วิธีการผลิตฟิล์มพลาสติกบางที่
บรรจุภัณฑ์มันรวมอัดรีดและเป่าเพื่อผลิตฟิล์มบางหลอด กระบวนการเริ่มต้น
กับรีดหลอดที่วาดขึ้นทันทีในขณะที่ยังหล่อและพร้อมกัน
ขยายขนาด โดยอากาศพองเป็นผ่านตายงูสายน้ำผึ้ง .
13.13 อธิบาย Calendering กระบวนการ .
ตอบ Calendering คือกระบวนการผลิตแผ่นและฟิล์มหุ้นออกของยาง หรือยาง
เช่น plasticized พลาสติกพีวีซี ในกระบวนการ วัตถุดิบเริ่มต้นคือผ่าน
ชุดม้วนงานวัสดุและลดความหนาที่ต้องการ เกตส์ พอลิเมอร์เส้นใยและเส้นใย
13.14 ถูกใช้ในงานหลาย ; สิ่งที่สำคัญที่สุดโปรแกรม
ในเชิงพาณิชย์ ?
ตอบ สิ่งทอ .
13.15 เทคนิค อะไรคือความแตกต่างระหว่างเส้นใยและเส้นใย ?
ตอบ เส้นใยเป็นเส้นบางยาวของวัสดุที่มีความยาวอย่างน้อย 100 เท่าของเส้นผ่านศูนย์กลาง ;
เส้นใยเป็นเส้นใยที่ยาวต่อเนื่อง
13.16 ระหว่างเส้นใยสังเคราะห์วัสดุ ซึ่งเป็นสิ่งที่สำคัญที่สุด
ตอบ โพลีเอสเตอร์เป็นสำคัญที่สุดในเชิงพาณิชย์ ตามด้วยไนลอน , acrylics , และเรยอน .
13.17 อธิบายสั้น ๆในกระบวนการฉีดขึ้นรูป .
ตอบการฉีดขึ้นรูปเป็นกระบวนการซึ่งเป็นพอลิเมอร์จะอุ่นให้รัฐสูงและพลาสติก
บังคับไหลภายใต้แรงดันสูงเข้าไปในโพรงแม่พิมพ์ ซึ่งรวมตัวกัน . ขึ้นรูปเป็นแล้ว

13.18 เอาออกจากช่อง เป็น เครื่องฉีดพลาสติก แบ่งเป็นองค์ประกอบหลักสอง ชื่อพวกเขา .
ตอบ ส่วนประกอบของเครื่องฉีดพลาสติก ( 1 ) หัวฉีด ( 2 )
หน่วยหนีบหน่วย .
มีค่าอะไรเป็นสองประเภทพื้นฐานของหนีบหน่วย ?
ตอบ ที่หนีบหน่วยคือ ( 1 ) และ ( 2 ) หนีบสลับเครื่องกลไฮดรอลิก นอกจากนี้ มี hydromechanical
เป็นหน่วยซึ่งรวมไฮโดรลิกและเครื่องกล actuations .
13.20 อะไรคือการทำงานของประตูในแม่พิมพ์ฉีด
ตอบการทำงานของประตูในการฉีดแม่พิมพ์คือการรัดการไหลของพลาสติกเหลวเข้าไปใน
โพรง ซึ่งเพิ่มอัตราเฉือนและลดความหนืดของพอลิเมอร์หลอมเหลว .
13.21 อะไรคือข้อดีของจานสามมากกว่าสองแผ่นแม่พิมพ์แม่พิมพ์ฉีดพลาสติก ?
ตอบ เป็นแม่พิมพ์เปิด สามแผ่นแม่พิมพ์โดยอัตโนมัติแยกแม่พิมพ์ส่วน ( s ) จากระบบทางวิ่ง
.
13