2. Materials and methodsAn experime

2. Materials and methods
An experimental resin matrix (BUT) was made by mixing Bis-
GMA, UDMA and TEGDMA in the ratio of 1:1:1 by weight.
Silane coated filler (average size: 1.55

m, Schott, Germany)
was added in the ratio of 50wt.% of resin composite. Pho-
toinitiator, accelerator and inhibitor [0.7% camphoroquinone,
0.35% 2-(dimethylamino) ethylmethacylate, and 0.05% buty-
lated hydroxytolune] were added. To determine the influ-
ence of concentration of FWA, FWA [1,4-double-(benzoxazole-
group-2-group)naphthalene, C
24
H
14
O
2
N
2
, CAS no. 5089-22-5]
was added in the concentrations of 0.01, 0.05 and 0.1% of the
resin composite. FWA was not added in the control group.
To determine the influence of resin matrix on fluorescent
emission, two resin mixtures composed of 60wt.% Bis-GMA
and 40wt.% TEGDMA (BT), and 60wt.% UDMA and 40wt.%
TEGDMA (UT) were made. Into these matrices, 50wt.% silane
coated filler was added. The same amount of photoinitiator,

ผลลัพธ์ (ไทย) 3:

2 . วัสดุและวิธีการ
เป็นเมทริกซ์เรซินทดลอง ( แต่ ) ทำโดยการผสมสอง
GMA udma tegdma , และในอัตราส่วน 1 : 1 : 1 โดยน้ำหนัก สารเคลือบ
เลน ( ขนาดเฉลี่ย 1.55

M คือ เยอรมนี )
เพิ่มในสัดส่วนของ 50wt % ของเรซิน คอมโพสิต โพธิ์ -
toinitiator , ตัวเร่งและตัวยับยั้ง [ camphoroquinone 0.7% , 0.35 %
2 - ( dimethylamino ) ethylmethacylate และ 0.05 % รองเท้าปิด -
สาย hydroxytolune ] เพิ่ม หา influ -
อิทธิพล ( ของความเข้มข้นของ FWA FWA , [ 1,4-double - เบนโซซาโซล -
group-2-group ) แมนดาริน , C
24
H
14
o
2
n
2
, หมายเลข CAS 5089-22-5 ]
เพิ่มในความเข้มข้น 0.01 , 0.05 และ 0.1% ของ
เรซิน คอมโพสิต FWA ไม่ได้เพิ่มในกลุ่มควบคุม
เพื่อศึกษาอิทธิพลของเรซินเมทริกซ์ในหลอด
มลพิษ2 เรซินผสมประกอบด้วย 60wt % ทวิย่า และ 40wt
% tegdma ( BT ) และ 60wt % udma และ 40wt %
tegdma ( UT ) ที่ถูกสร้างขึ้น เป็นเมทริกซ์เหล่านี้ 50wt % สารเคลือบเลน
ถูกเพิ่มเข้ามา photoinitiator จํานวนเดียวกัน ,