After cold rolling at a reduction of 87.5% and subsequent annealing treatment at 698K for 25min,a fine microstructure with nanosized α precipitates
distributed insmall β grains as well as high density of dislocations was obtained to achieve a yield strength of 720MPa and a ultimate tensile
strength of 860MPa.