The uniform dispersion of NBRr in the SBR matrix altered the crack path, which leads to more resistance for crack ropagation and, hence, higher tensile strength. The presence of more tear lines on the fracture surfaces of SBR/NBRr blends with ENR-
50 designates the effect of increased interaction between phases, thus improving the compatibility and enhancing the tensile strength.