It should be noted that the high-resolution SEM
observation of samples aged at lower temperatures was not possible
without the beam deceleration technique owing to the large
amount of beam damage. The structural order, period and pore size
of SBA-15 increased with aging temperature, and agreed well with
XRD and N2 adsorption/desorption measurements.