Form Table 1.2 you can see that lattice parameter increases with increasing 2θ values. Since the systematic error in sin²θ decreases as θ increases, you should select the value of a for the highest-angle peak in the diffraction pattern as the most accurate. (See Experimental Module 3 for precise lattice parameter measurements.)