The resistivity of the film was 1.1 × 10−2 cm, and its transmittance at 550 nm was 95%. It should be noted that ITO films prepared via the sintering of ITO nanoparticles have porous structures consisting of more-or-less-sintered nanoparticles, rather than continuous and homogenous structures