Tanigels were prepared according to

Tanigels were prepared according to the basis of Nakano et al.
[9]. Five grams of tannin extract were dissolved in 32mL of NaOH
(PANREAC) 0.125 mol L−1 and 30mL of distilled water at 80 ◦C.
When mixture was homogeneous, certain amount of aldehyde
were added and reaction was kept at the same temperature for 8 h
until polymerization was considered completed. Then, the apparent
gummy product was lead to complete evaporation of water
remain and dried in oven (65 ◦C) overnight. After drying, tannin
rigid gels were crushed and sieved to produced 38–53m diameter
particles. They were washed successively with distilled water
and HNO3 0.01 mol L−1 (PANREAC) to remove unreacted sodium
hydroxide. Finally, the adsorbent was dried again in oven. Differences
are found between this preparation way and the description
made by Yurtsever and Sengil [17], mainly concerning the amount
of formaldehyde.

ผลลัพธ์ (ไทย) 2:

Tanigels Tanigels were prepared according to the basis of Nakano et al.
[ ห้ากรัมสารสกัดแทนนินของถูกกลืนหายไปใน [9]. Five grams of tannin extract were dissolved in 32mL of NaOH
(PANREAC) 0.125 mol L (PANREAC) 0.125 mol L- −1 ◦ 8 ชั่วโมงจนพอลิเมอได้รับการพิจารณาแล้วเสร็จ จากนั้นเห็นได้ชัดผลิตภัณฑ์เหนียวก็นำไปสู่การดำเนินการการระเหยของน้ำยังคงอยู่และแห้งในเตาอบ( ◦ C) 1 and 30mL of distilled water at 80 ◦C.
When mixture was homogeneous, certain amount of aldehyde
were added and reaction was kept at the same temperature for 8 h
until polymerization was considered completed. Then, the apparent
gummy product was lead to complete evaporation of water
remain and dried in oven (65 ◦C) overnight. After drying, tannin
rigid gels were crushed and sieved to produced 38–53m diameter
particles. They were washed successively with distilled water
and HNO3 0.01 mol L−1 (PANREAC) to remove unreacted sodium
hydroxide. Finally, the adsorbent was dried again in oven. Differences
are found between this preparation way and the description
made by Yurtsever and Sengil [17], mainly concerning the amount
of formaldehyde.

ผลลัพธ์ (ไทย) 3:

tanigels เตรียมตามพื้นฐานของนากาโนะ et al .
[ 9 ] 5 กรัมสารสกัดแทนนินที่ละลายใน 32ml ใช้
( panreac 0.125 mol − 1 L ) 30ml ของน้ำกลั่นที่ 80 ◦ C .
เมื่อผสมเป็นเนื้อเดียวกันจำนวนหนึ่งของ aldehydes
เพิ่มปฏิกิริยาที่ถูกเก็บไว้ที่อุณหภูมิเดียวกัน 8 H
จนเกิดเป็นความสำเร็จ แล้วปรากฏ
ผลิตภัณฑ์กัมมี่ถูกทำให้สมบูรณ์ การระเหยของน้ำ
ยังคงอยู่ และแห้งในเตาอบ ( 65 ◦ C ) ในชั่วข้ามคืน หลังจากการอบแห้งแข็งและแทนนิน
เจลถูกบดขยี้อีกครั้ง ผลิต 38 – 53  เมตร
อนุภาค พวกเขาล้างอย่างต่อเนื่องกับน้ำกลั่นและ 0.01 โมลต่อลิตร
กรดดินประสิว− 1 ( panreac ) เพื่อลบเข้าสู่
โซเดียม ไฮดรอกไซด์ ในที่สุด ใช้แล้วแห้งอีกครั้งในเตาอบ ความแตกต่าง
ระหว่างนี้เตรียมพบวิธีและรายละเอียด
โดย yurtsever sengil [ 17 ] และส่วนใหญ่เกี่ยวกับยอดเงิน
ของฟอร์มาลดีไฮด์