The mechanism of MB degradation was studied by monitoring
CO2 during PEC process. Fig. 8A shows that the increase of CO2
concentration is correlated with the % MB degradation. Thus, it was
confirmed that the final product was CO2 as suggested from the
fact that the absorption spectra of MB in the degradation process
showed no other absorption peaks.