where DHm and DHc are the enthalpies of melting and cold crystallization during the heating, respectively; DHom is the enthalpy assuming 100% crystalline PLA homopolymers (93.7 J/g), [29] and wf is the weight fraction of PLA component in the blend.
where DHm and DHc are the enthalpies of melting and cold crystallization during the heating, respectively; DHomis the enthalpy assuming 100% crystalline PLA homopolymers (93.7 J/g), [29] and wf is the weight fraction of PLAcomponent in the blend.