AbstractThermal and optical propert

Abstract
Thermal and optical properties of ternary phosphate glasses prepared by conventional melt-quenching technique, belonging to the series (50 − X)BaO–XCaF2–50P2O5 (X = 0 to 10 mol%) were investigated with increase in CaF2 content. Thermal stability and glass forming ability studied using differential thermal analysis (DTA) were found to increase with the increase in CaF2 content. Powder X-ray diffraction (XRD) analysis of heat treated samples also revealed that CaF2 addition improves the thermal stability against crystallization. Increase in both glass transition temperature and onset crystallization temperature with the increase in CaF2 content can be attributed to the partial substitution of Ba2 + ion with Ca2 + ion, which is having larger field strength. The observed decrease in the melting temperature of glass batch with the increase in CaF2 content indicates that CaF2 acts as a flux and reduces the viscosity of the glass melt. The decrease in refractive index of the glasses with the increase in CaF2 content can be attributed to replacement of lower field strength Ba2 + by Ca2 + or the partial substitution of more polarizable oxygen ion by fluorine. Optical band gap energy slightly increased and Urbach energy marginally reduced with the increase in CaF2 content. Increase in optical band gap energy was further confirmed by calculating theoretical optical basicity of glasses. Average anion polarizability (αO/F) of (50 − X)BaO–XCaF2–50P2O5 glasses calculated from refractivity data using Lorentz–Lorentz relation was correlated with its theoretical optical basicity (λth) using the previously established correlation for oxyfluoro phosphate glasses.

ผลลัพธ์ (ไทย) 1:

บทคัดย่อThermal and optical properties of ternary phosphate glasses prepared by conventional melt-quenching technique, belonging to the series (50 − X)BaO–XCaF2–50P2O5 (X = 0 to 10 mol%) were investigated with increase in CaF2 content. Thermal stability and glass forming ability studied using differential thermal analysis (DTA) were found to increase with the increase in CaF2 content. Powder X-ray diffraction (XRD) analysis of heat treated samples also revealed that CaF2 addition improves the thermal stability against crystallization. Increase in both glass transition temperature and onset crystallization temperature with the increase in CaF2 content can be attributed to the partial substitution of Ba2 + ion with Ca2 + ion, which is having larger field strength. The observed decrease in the melting temperature of glass batch with the increase in CaF2 content indicates that CaF2 acts as a flux and reduces the viscosity of the glass melt. The decrease in refractive index of the glasses with the increase in CaF2 content can be attributed to replacement of lower field strength Ba2 + by Ca2 + or the partial substitution of more polarizable oxygen ion by fluorine. Optical band gap energy slightly increased and Urbach energy marginally reduced with the increase in CaF2 content. Increase in optical band gap energy was further confirmed by calculating theoretical optical basicity of glasses. Average anion polarizability (αO/F) of (50 − X)BaO–XCaF2–50P2O5 glasses calculated from refractivity data using Lorentz–Lorentz relation was correlated with its theoretical optical basicity (λth) using the previously established correlation for oxyfluoro phosphate glasses.

ผลลัพธ์ (ไทย) 2:

บทคัดย่อสมบัติทางความร้อนและแสงของแว่นตาฟอสเฟต ternary จัดทำขึ้นโดยใช้เทคนิคการละลายดับธรรมดาที่เป็นซีรีส์ (50 - X) เบ้า XCaF2-50P2O5 (X = 0-10 mol%) ได้รับการตรวจสอบด้วยการเพิ่มเนื้อหา CaF2
เสถียรภาพทางความร้อนและความสามารถในการขึ้นรูปแก้วศึกษาโดยใช้การวิเคราะห์ความร้อนที่แตกต่างกัน (DTA) พบว่าจะเพิ่มขึ้นด้วยการเพิ่มเนื้อหา CaF2 ผง X-ray diffraction (XRD) การวิเคราะห์ของกลุ่มตัวอย่างได้รับการรักษาความร้อนยังเผยว่านอกจาก CaF2 ช่วยเพิ่มเสถียรภาพทางความร้อนกับการตกผลึก เพิ่มขึ้นทั้งในอุณหภูมิการเปลี่ยนกระจกและอุณหภูมิการตกผลึกการโจมตีด้วยการเพิ่มเนื้อหา CaF2 สามารถนำมาประกอบกับการเปลี่ยนตัวผู้เล่นบางส่วนของ Ba2 + ไอออนกับ Ca2 + ไอออนซึ่งจะมีความแรงของสนามที่มีขนาดใหญ่ การลดลงสังเกตได้ในอุณหภูมิหลอมเหลวของชุดแก้วที่มีการเพิ่มขึ้นในเนื้อหา CaF2 แสดงให้เห็นว่า CaF2 ทำหน้าที่เป็นฟลักซ์และลดความหนืดของละลายแก้ว การลดลงของดัชนีหักเหของแก้วที่มีการเพิ่มขึ้นในเนื้อหา CaF2 ที่สามารถนำมาประกอบกับการเปลี่ยนของความแรงของสนามที่ต่ำกว่า Ba2 + โดย Ca2 + หรือการเปลี่ยนตัวผู้เล่นบางส่วนของออกซิเจนไอออน polarizable มากขึ้นโดยฟลูออรีน ช่องว่างแถบพลังงานออฟติคอลเพิ่มขึ้นเล็กน้อยและพลังงานลดลงเล็กน้อย Urbach ด้วยการเพิ่มเนื้อหา CaF2 เพิ่มขึ้นในช่องว่างแถบพลังงานแสงได้รับการยืนยันต่อไปโดยการคำนวณทางทฤษฎีด่างแสงของแว่นตา polarizability ไอออนเฉลี่ย (αO / F) ของ (50 - X) แก้วเบ้า XCaF2-50P2O5 คำนวณจากข้อมูลการใช้ความสัมพันธ์ refractivity Lorentz-อเรนซ์มีความสัมพันธ์กับด่างแสงทฤษฎี (λth) โดยใช้ความสัมพันธ์ที่จัดตั้งขึ้นก่อนหน้านี้สำหรับแว่นตาฟอสเฟต oxyfluoro