In this experimental study, the effects of 10, 20, 25, 30 and 40 wt.% pumice addition on properties of
blended cement pastes and mortars were investigated. Pumice blended cements with a high fineness
were produced by intergrinding Portland cement clinker, pumice and gypsum. Characteristics such as
particle size distribution, soundness, setting times, chemical analysis, compressive and bending
strengths, drying shrinkage, autoclave expansion and sulfate resistance were determined. In addition,
the microstructures of some samples scanned by scanning electron microscopy were photographed.
Compressive strengths of mortars produced with pumice blended cements were lower than that of
Portland cement tested ages up to 360 days. Pumice blended cements increase durability, sulfate expansion,
shrinkage and autoclave expansion.
ในการศึกษานี้ได้ศึกษาผลของ 10 , 20 , 25 , 30 และ 40 โดยน้ำหนัก นอกจากคุณสมบัติของหินภูเขาไฟผสมซีเมนต์เพสต์ และถูกสอบสวน หินภูเขาไฟผสมซีเมนต์ที่มีความละเอียดสูงถูกผลิตโดย intergrinding เม็ดปูนซีเมนต์ , หิน และยิปซัม ลักษณะ เช่นขนาดอนุภาคกระจายความแข็งแรง , การตั้งค่าเวลา , การวิเคราะห์ทางเคมี กำลังอัด กำลังดัดจุดแข็ง การหดตัวแบบแห้งและเครื่องนึ่งเพิ่มความต้านทานซัลเฟต คือกำหนด นอกจากนี้โครงสร้างของตัวอย่างบางส่วนที่สแกนโดยกล้องจุลทรรศน์อิเล็กตรอนแบบส่องกราดถูกถ่ายภาพกำลังรับแรงอัดของมอร์ต้าร์ซีเมนต์ผสมกับหินภูเขาไฟผลิตต่ำกว่าที่ของปูนซีเมนต์ปอร์ตแลนด์ทดสอบอายุถึง 360 วัน การเพิ่มความทนทานของซีเมนต์ผสมหินภูเขาไฟ , ซัลเฟตการหดและขยายตัวหม้ .